Magnetic PLGA microspheres loaded with SPIONs promoted the reconstruction of bone defects through regulating the bone mesenchymal stem cells under an external magnetic field.

Superparamagnetic iron oxide nanoparticles (SPIONs) have been presented to regulate the migration and osteogenic differentiation of bone mesenchymal stem cells (BMSCs) under magnetic field (MF). However, the toxicity and short residence for the massively exposed SPIONs at bone defects compromises their practical application. Herein, SPIONs were encapsulated into PLGA microspheres to overcome these shortcomings. Three types of PLGA microspheres (PFe-I, PFe-II and PFe-III) were prepared by adjusting the feeding amount of SPIONs, in which the practical SPIONs loading amounts was 1.83%, 1.38% and 1.16%, respectively. The average diameter of the fabricated microspheres ranged from 160 μm to 200 μm, having the porous and rough surfaces displayed by SEM. Moreover, they displayed the magnetic property with a saturation magnetization of 0.16 emu/g. In vitro cell studies showed that most of BMSCs were adhered on the surface of PFe-II microspheres after 2 days of co-culture. Moreover, the osteoblasts differentiation of BMSCs was significantly promoted by PFe-II microspheres after 2 weeks of co-culture, as shown by detecting osteogenesis-related proteins expressions of ALP, COLI, OPN and OCN. Afterward, PFe-II microspheres were surgically implanted into the defect zone of rat femoral bone, followed by exposure to an external MF, to evaluate their bone repairing effect in vivo. At 6th week after treatment with PFe-II + MF, the bone mineral density (BMD, 263.97 ± 25.99 mg/cm), trabecular thickness (TB.TH, 0.58 ± 0.08 mm), and bone tissue volume/total tissue volume (BV/TV, 78.28 ± 5.01%) at the defect zone were markedly higher than that of the PFe-II microspheres alone (BMD, 194.34 ± 26.71 mg/cm; TB.TH, 0.41 ± 0.07 mm; BV/TV, 50.49 ± 6.41%). Moreover, the higher expressions of ALP, COLI, OPN and OCN in PFe-II + MF group were displayed in the repairing bone. Collectively, magnetic PLGA microspheres together with MF may be a promising strategy for repairing bone defects.