Nanoscale phase management of the 2D/3D heterostructure toward efficient perovskite solar cells.

The stabilization of the formamidinium lead iodide (FAPbI) structure is pivotal for the development of efficient photovoltaic devices. Employing two-dimensional (2D) layers to passivate the three-dimensional (3D) perovskite is essential for maintaining the α-phase of FAPbI and enhancing the power conversion efficiency (PCE) of perovskite solar cells (PSCs). However, the role of bulky ligands in the phase management of 2D perovskites, crucial for the stabilization of FAPbI, has not yet been elucidated. In this study, we synthesized nanoscale 2D perovskite capping crusts with  = 1 and 2 Ruddlesden-Popper (RP) perovskite layers, respectively, which form a type-II 2D/3D heterostructure. This heterostructure stabilizes the α-phase of FAPbI, and facilitates ultrafast carrier extraction from the 3D perovskite network to transport contact layer. We introduced tri-fluorinated ligands to mitigate defects caused by the halide vacancies and uncoordinated Pb ions, thereby reducing nonradiative carrier recombination and extending carrier lifetime. The films produced were incorporated into PSCs that not only achieved a PCE of 25.39% but also maintained 95% of their initial efficiency after 2000 h of continuous light exposure without encapsulation. These findings underscore the effectiveness of a phase-pure 2D/3D heterostructure-terminated film in inhibiting phase transitions passivating the iodide anion vacancy defects, facilitating the charge carrier extraction, and boosting the performance of optoelectronic devices.