Article Abstract
Objective: To prepare porous core-shell composite particles (PCPs) in order to improve the flowability and compactibility of powder materials for direct compaction (DC), as well as the dissolution of tablets.
Significance: The results obtained are meaningful to boosting the development and further research of PCPs on DC. Methods: In this study, hydroxypropyl methylcellulose (HPMC E3) and polyvinylpyrrolidone (PVP K30) were selected as shell materials, the Xiao Er Xi Shi formulation powder (XEXS) was used as the core materials, ammonium bicarbonate (NHHCO), and sodium bicarbonate (NaHCO) were employed as pore-forming agent. Using co-spray drying method to prepare composite particles (CPs). Then, the physical properties and comparison between different CPs were characterized comprehensively. Finally, the different CPs were directly compacted as tablets to explore the effect on the dissolution behavior of DC tablets, respectively.
Results: (i) The XEXS PCPs were prepared successfully by co-spray drying, and the yield of PCPs is almost 80%; (ii) The TS values of PCP-X-P-Na, PCP-X-P-NH, PCP-X-H-Na and PCP-X-P-Na were 5.70, 7.56, 3.98, and 6.88 times higher than that of raw material (X); (iii) The disintegration time of PCPs tablets decreased 10-25% when compared with CPs tablets; (iv) The values of Carr's index (CI), Hausner ratio (HR), Caking strength (CS), and Cohesion index (CoI) of PCP-X-H-NH were 19.16%, 19.29%, 40.14%, and 6.39% lower than that of X, respectively.
Conclusions: The PCPs prepared by co-spray drying did improve the flowability and compactibility of powder, as well as the dissolution of tablets.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1080/03639045.2023.2197070 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Comparison of shear bond strengths of clear aligner attachments to full-contour zirconia crowns with different sandblasting times and primers: An in vitro study.
Am J Orthod Dentofacial Orthop
September 2025
Department of Orthodontics, Faculty of Dentistry, Phenikaa University, Duong Noi, Hanoi, Vietnam.
Introduction: This study investigated the effect of sandblasting time and primer type on the shear bond strength of composite attachments to full-contour zirconia crowns.
Methods: A total of 108 zirconia specimens were fabricated and divided into 9 groups (n = 12) according to sandblasting time (10, 30, and 60 seconds) and primer type (silane, 10-methacryloyloxydecyl dihydrogen phosphate [MDP], universal). After sandblasting with 110-μm alumina particles, specimens were primed, and attachments were bonded using a packable composite.
Chemically Lithiated Poly(vinylidene difluoride) with In Situ Generated LiF Nanofiller as Hybrid Artificial Layer for Stable Lithium Metal Anodes.
Small
September 2025
Key Laboratory of Electrochemical Power Sources of Hubei Province, College of Chemistry and Molecular Sciences, Wuhan University, Wuhan, 430072, China.
Hybrid artificial layer based on inorganic/polymer composite endows superior toughness and mechanical strength, which can achieve high stability of lithium metal anode. However, the large particle size and uneven distribution of inorganic fillers hinder the uniform flow of lithium ions across the membrane, making it difficult to achieve smooth lithium metal deposition/stripping. In this work, a chemical lithiation-induced defluorination strategy is proposed to engineer poly(vinylidene difluoride) (PVDF)-based artificial layers, enabling in situ incorporation of highly dispersed LiF nanofiller within the polymer matrix and precise control over the LiF content.
View Article and Find Full Text PDFEffect of preparation method on the structure and properties of kaempferol-loaded zein-gum arabic nanoparticles.
J Sci Food Agric
September 2025
College of Food Science & Technology, Shanghai Ocean University, Shanghai, China.
Background: Kaempferol (KAE), a bioactive flavonoid, has limited solubility and stability in water. Zein-gum arabic (GA) nanoparticles (NPs) are promising carriers for KAE, but the influence of preparation methods on their structure and properties remains unclear. This study investigated the effect of preparation method on the structure and properties of KAE-loaded zein-GA NPs.
View Article and Find Full Text PDFOptimal cerium microalloying enhances SASS/Q235 weld corrosion and antibacterial performance.
iScience
September 2025
State Key Laboratory of Advanced Marine Materials, Institute of Oceanology, Chinese Academy of Sciences, Qingdao 266071, China.
Super austenitic stainless steels (SASS) face challenges like galvanic corrosion and antibacterial performance when welded to carbon steel (Q235) in marine environments. This study demonstrates that adding 1.0 wt% cerium (Ce) to SASS refines the heat-affected zone (HAZ) grain structure (from 7 μm to 2 μm), suppresses detrimental σ-phase precipitation, and forms a dense oxide film.
View Article and Find Full Text PDFEfficient methylene blue elimination from water media by nanocomposite adsorbent-based carboxymethyl cellulose-grafted poly(acrylamide)/magnetic biochar decorated with ZIF-67.
RSC Adv
September 2025
Saveetha School of Engineering, Saveetha Institute of Medical and Technical Sciences, Saveetha University Chennai Tamil Nadu 602105 India.
A free radical polymerization approach was applied to synthesize different carboxymethyl cellulose-grafted poly(acrylamide) hydrogels (Hyd) composited with biochar, magnetic biochar, and magnetic biochar decorated with ZIF-67 to decontaminate methylene blue (MB) from water media. Biochar was obtained from walnut shells (WS) by a pyrolysis method, and magnetic biochar (WS/CoFeO) and biochar-decorated ZIF-67 (WS/CoFeO/ZIF-67) were prepared by chemical co-precipitation and hydrothermal methods, respectively. An increase in the amount of these particles by up to 10 wt% enhanced the removal performance.
View Article and Find Full Text PDF