Enhanced biomineralization of shape memory composite scaffolds from citrate functionalized amorphous calcium phosphate for bone repair.

Traditional shape memory polymers (SMPs) could avoid large volume trauma during implantation; however, for bone repair, scaffolds with high porosity and biomineralization are essential to promote bone regeneration. A novel porous composite scaffold with high biomineralization activity was developed by sequential gas foaming and a freeze-drying method. The results showed that the cross-linked block structure of the polymer matrix presented excellent shape memory properties, and osteogenesis was promoted by citrate functionalized amorphous calcium phosphate (CCACP). CCACP improved the mechanical strength of the scaffold, and the synergistic effect of CCACP and PEG promotes hydrophilicity and further promoted cell adhesion. Bending experiments indicated that the shape-memory effect of the scaffolds could be varied by varying the CCACP content. In addition, hydroxyapatite deposition was sped up as CCACP accelerated the mineralization of the scaffolds. Moreover, the result of the CCK-8 assessment suggested that composite scaffolds exhibited high biocompatibility, and the cells extended out abundant filopodia to adhere onto the scaffolds. In rat bone defect models, the obtained scaffolds promoted new bone formation compared to the control group. The developed composite scaffolds show potential for minimally invasive bone repair application.