Article Abstract
In order to better understand the damage tolerance of reinforced composite plates, the impact damage of the reinforced composite plates was investigated under low-velocity impact test. The experimental results show that the impact of different positions and energies causes different degrees of damage to the specimens, including but not limited to ply fracture, internal delamination of the skin, and debonding of the stiffeners and skin. After impacting, the specimens were tested in an axial compression. The results show that the ultimate bearing capacity of the specimen is also affected by different forms of impact. The impact point has the greatest influence on the specimen while it locates at the intersection of longitudinal and transverse bars. Compared with the intact specimen, the ultimate load carrying capacity was reduced by 16.83% and 44.02%, while the specimen impacted by 15 J and 30 J, respectively. The compression failure mode of the damaged specimen is mainly the breakage of the stiffeners and the delamination of the skin.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC7321590 | PMC |
| http://dx.doi.org/10.3390/ma13112573 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Experimental study on polymer friction composite with natural friction modifiers for brake pads.
PLoS One
September 2025
Department of Industrial Engineering, College of Engineering, King Saud University, Riyadh, Saudi Arabia.
The increasing concern over environmental pollution from brake dust and the adverse impacts of conventional brake pad materials, such as metallic, semi-metallic, and ceramic composites, has prompted the exploration of more sustainable alternatives. Traditional brake pads release harmful non-exhaust emissions that contribute to air pollution and wear down quickly, posing both environmental and operational challenges. This study investigates the development and performance evaluation of polymer friction composites enhanced with natural friction modifiers sourced from agricultural waste materials like walnut shell, coconut shell, and groundnut shell powders.
View Article and Find Full Text PDFCrystallization and crystal morphology of polymers: A multiphase-field study.
J Thermoplast Compos Mater
August 2025
Institute for Applied Materials - Microstructure Modeling and Simulation, Karlsruhe Institute of Technology (KIT), Karlsruhe, Germany.
In this paper, we introduce a coarse-grained model of polymer crystallization using a multiphase-field approach. The model combines a multiphase-field method, Nakamura's kinetic equation, and the equation of heat conduction for studying microstructural evolution of crystallization under isothermal and non-isothermal conditions. The multiphase-field method provides flexibility in adding any number of phases with different properties making the model effective in studying blends or composite materials.
View Article and Find Full Text PDFSolvent-free fabrication of TPU-reinforced PE/carbon composites for high-performance positive temperature coefficient materials in lithium-ion battery safety.
RSC Adv
September 2025
State Key Laboratory of Disaster Prevention & Reduction for Power Grid Changsha China
Positive temperature coefficient (PTC) materials are pivotal for safeguarding lithium iron phosphate batteries, yet their industrial application is hindered by critical drawbacks: excessive film thickness, high internal resistance, and poor solvent sustainability. Addressing these challenges, this study innovatively develops a solvent-free thermal rolling process to fabricate an asymmetric expansion polymer film, specifically thermoplastic polyurethane (TPU) reinforced polyethylene (PE)/carbon composites, which significantly enhances the PTC effect. The core mechanism lies in the asymmetric thermal expansion of TPU and PE: this unique behavior disrupts the conductive carbon network, triggering a sharp PTC transition at around 120 °C.
View Article and Find Full Text PDFAC corona aging behavior and performance comparison of HTV silicone rubber, cycloaliphatic epoxy resin, and glass fiber-reinforced epoxy used in composite insulators.
RSC Adv
August 2025
State Key Laboratory of Electrical Insulation and Power Equipment, Xi'an Jiaotong University Xi'an Shaanxi 710049 China
Cycloaliphatic epoxy resin (CEP) is a promising candidate for rigid housings in high-voltage composite insulators due to its superior hardness, water resistance, and interfacial adhesion compared with conventional high-temperature vulcanized silicone rubber (HTV-SR). However, the long-term insulation degradation mechanisms of CEP under corona discharge are still not fully understood. In this study, CEP, HTV-SR, and glass fiber-reinforced epoxy (GFRP) were subjected to AC corona aging using a multi-needle plate electrode.
View Article and Find Full Text PDFSacubitril/valsartan versus enalapril in chronic Chagas cardiomyopathy with heart failure: Baseline characteristics of the PARACHUTE-HF trial.
Eur J Heart Fail
September 2025
Brazilian Clinical Research Institute (BCRI), São Paulo, Brazil.
Aims: The PARACHUTE-HF trial (NCT04023227) is evaluating the effect of sacubitril/valsartan compared with enalapril on a hierarchical composite of cardiovascular events (cardiovascular death, first heart failure hospitalization), and change in N-terminal pro-B-type natriuretic peptide (NT-proBNP) levels in participants with heart failure and reduced ejection fraction (HFrEF) caused by chronic Chagas cardiomyopathy (CCC). We describe the baseline characteristics of participants in PARACHUTE-HF compared with prior HFrEF trials.
Methods And Results: PARACHUTE-HF, a multicentre, active-controlled, open-label trial, enrolled 922 participants with confirmed CCC, New York Heart Association (NYHA) functional class II-IV, and left ventricular ejection fraction (LVEF) ≤40%.