Incorporation of manganese dioxide within ultraporous activated graphene for high-performance electrochemical capacitors.

Manganese dioxide (MnO(2)) particles 2-3 nm in size were deposited onto a porous "activated microwave expanded graphite oxide" (aMEGO) carbon scaffold via a self-controlled redox process. Symmetric electrochemical capacitors were fabricated that yielded a specific capacitance of 256 F/g (volumetric: 640 F/cm(3)) and a capacitance retention of 87.7% after 1000 cycles in 1 M H(2)SO(4); when normalized to MnO(2), the specific capacitance was 850 F/g.

Nanostructured hybrid transparent conductive films with antibacterial properties.

Here, we demonstrate that the assembly of nanostructures with different dimensionalities yields "multicomponent hybrid" transparent conductive films (TCFs) with sheet resistance and optical transmittance comparable to that of indium tin oxide (ITO) films. It was shown that sheet resistance of single-component Ag nanowire (NW) films can be further decreased by introducing gold-decorated reduced graphene oxide (RG-O) nanoplatelets that bridge the closely located noncontacting metal NWs. RG-O nanoplatelets can act as a protective and adhesive layer for underneath metal NWs, resulting in better performance of hybrid TCFs compared to single-component TCFs.

Highly conductive and porous activated reduced graphene oxide films for high-power supercapacitors.

We present a novel method to prepare highly conductive, free-standing, and flexible porous carbon thin films by chemical activation of reduced graphene oxide paper. These flexible carbon thin films possess a very high specific surface area of 2400 m(2) g(-1) with a high in-plane electrical conductivity of 5880 S m(-1). This is the highest specific surface area for a free-standing carbon film reported to date.

Activated graphene as a cathode material for Li-ion hybrid supercapacitors.

Chemically activated graphene ('activated microwave expanded graphite oxide', a-MEGO) was used as a cathode material for Li-ion hybrid supercapacitors. The performance of a-MEGO was first verified with Li-ion electrolyte in a symmetrical supercapacitor cell. Hybrid supercapacitors were then constructed with a-MEGO as the cathode and with either graphite or Li(4)Ti(5)O(12) (LTO) for the anode materials.

Carbon-based supercapacitors produced by activation of graphene.

Supercapacitors, also called ultracapacitors or electrochemical capacitors, store electrical charge on high-surface-area conducting materials. Their widespread use is limited by their low energy storage density and relatively high effective series resistance. Using chemical activation of exfoliated graphite oxide, we synthesized a porous carbon with a Brunauer-Emmett-Teller surface area of up to 3100 square meters per gram, a high electrical conductivity, and a low oxygen and hydrogen content.

Nanostructured reduced graphene oxide/Fe2O3 composite as a high-performance anode material for lithium ion batteries.

Reduced graphene oxide/Fe(2)O(3) composite was prepared using a facile two-step synthesis by homogeneous precipitation and subsequent reduction of the G-O with hydrazine under microwave irradiation to yield reduced graphene oxide (RG-O) platelets decorated with Fe(2)O(3) nanoparticles. As an anode material for Li-ion batteries, the RG-O/Fe(2)O(3) composite exhibited discharge and charge capacities of 1693 and 1227 mAh/g, respectively, normalized to the mass of Fe(2)O(3) in the composite (and ∼1355 and 982 mAh/g, respectively, based on the total mass of the composite), with good cycling performance and rate capability. Characterization shows that the Fe(2)O(3) nanoparticles are uniformly distributed on the surface of the RG-O platelets in the composite.

Mesoporous carbon capsules as electrode materials in electrochemical double layer capacitors.

The performance of mesoporous carbon capsules as electrode materials in electrochemical double layer capacitors (EDLCs) was evaluated in the presence of a variety of electrolytes, including room temperature ionic liquids (ILs).

Exfoliation of graphite oxide in propylene carbonate and thermal reduction of the resulting graphene oxide platelets.

Graphite oxide was exfoliated and dispersed in propylene carbonate (PC) by bath sonication. Heating the graphene oxide suspensions at 150 degrees C significantly reduced the graphene oxide platelets; paper samples comprising such reduced graphene oxide platelets had an electrical conductivity of 5230 S/m. By adding tetraethylammonium tetrafluoroborate (TEA BF(4)) to the reduced graphene oxide/PC slurry and making a two-cell ultracapacitor, specific capacitance values of about 120 F/g were obtained.

Graphene-based ultracapacitors.

The surface area of a single graphene sheet is 2630 m(2)/g, substantially higher than values derived from BET surface area measurements of activated carbons used in current electrochemical double layer capacitors. Our group has pioneered a new carbon material that we call chemically modified graphene (CMG). CMG materials are made from 1-atom thick sheets of carbon, functionalized as needed, and here we demonstrate in an ultracapacitor cell their performance.