Could the sealer thickness affect the filling ability of bioceramic endodontic materials? Evaluation in a simulated physiological condition.

Context: Bioceramic sealers must provide filling and dimensional stability over time.

Aims: To evaluate by micro-computed tomography (micro-CT), the effect of sealer thickness on the physical properties of Bio-C Sealer (BCS) and BioRoot RCS (BR) after immersion in phosphate-buffered saline (PBS) for 7 and 30 days.

Materials And Methods: Extracted bovine teeth were prepared with ProDesign Logic 40/0.

Physicochemical and antibiofilm properties of new ready-to-use and powder/gel bioceramic endodontic sealers.

NeoSealer Flo (NSF) is a novel ready-to-use endodontic bioceramic sealer, and NeoMTA2 (NMTA2) is a powder-gel bioceramic used as a repair or filling material. Setting time (ST), pH, solubility, radiopacity, and flow were evaluated in accordance with the ISO 6876:2012 standards for NSF and NMTA2, in comparison with Bio-C Sealer (BCS) and AH Plus Jet (AHP). Bond strength was assessed using the push-out test.

Influence of Bioceramic Clinker particle size, radiopacifier, and liquids on their physicochemical properties.

This study evaluated the addition of calcium tungstate (CaWO4) as a radiopacifier and the manipulation with distilled water (DW) or liquid with additives (LA) on the physicochemical properties of Clinker (CL; Angelus) with different particle sizes (2 to 30 µm and <2 µm), compared to White MTA and MTA Repair HP. Initial and final setting times (ST) were evaluated according to ISO 6876:2012 and ASTM C266-03 standards. Radiopacity was assessed following ISO guidelines, and solubility was evaluated after immersion in distilled water or phosphate-buffered saline for 7 days.

Effectiveness and safety of three NiTi systems in endodontic retreatment of MB1 and MB2 root canals: a micro-CT and CBCT combined analysis.

Objective: To evaluate the performance in endodontic retreatment and pericervical dentin preservation using ProDesign Logic (PDL), Reciproc Blue (RB), and WaveOne Gold (WOG) NiTi systems in first (MB1) and second (MB2) mesiobuccal root canals of maxillary molars, using cone-beam computed tomography (CBCT) and micro-computed tomography (micro-CT).

Materials And Methods: MB1 and MB2 canals were prepared, filled, and randomized into four groups (n = 8). MB1 were retreated using PDL up to file 40/0.

Antimicrobial efficacy of natural-based endodontic solutions: a systematic review with a network meta-analysis.

This systematic review aims to provide preclinical evidence of the antimicrobial efficacy of natural endodontic solutions (NES) compared to sodium hypochlorite (NaOCl) and chlorhexidine (CHX) against Enterococcus faecalis. The study followed the PRISMA guidelines and had a registered protocol (PROSPERO - CRD42021224022). The inclusion criteria comprised ex vivo studies simulating root canal irrigation to assess the standardized mean difference of colony-forming units (CFUs).

Calcium silicate-based intracanal medication: Physicochemical properties and effectiveness of techniques for removing medication from the human root canal.

Objective: Our purpose was to investigate the physicochemical properties of Bio-C Temp, a bioceramic intracanal medication, and whether its residues remain adhered to the dentine walls after conventional manual irrigation (CMI) or passive ultrasonic irrigation (PUI) in comparison to Calen.

Methods: The pH after 12 hours, 1 day, 3 days, 7 days, 14 days, 21 days and 28 days, and the flow, radiopacity, and the solubility of the medications after immersion for 7 and 30 days in distilled water (dH2O) or phosphate-buffered saline (PBS) solution were evaluated. Filling capacity, and volumetric changes after 14 days were assessed by micro-computed tomography (micro-CT).

Volumetric change of calcium silicate-based repair materials in a simulated inflammatory environment: A micro-computed tomography study.

Context: An acidic hydrogen potential (pH) in an inflammatory condition in the periapical tissues may affect the properties of repair bioceramic cement.

Aims: The aim of this study was to evaluate the effect of pH on the volumetric change of the ready-to-use bioceramic NeoPUTTY (NP) compared to the powder/liquid MTA Repair HP (MTAHP) after immersion in butyric acid (BA, pH 4.1) or phosphate-buffered saline (PBS, pH 7.

In vivo method to evaluate volumetric changes in bioceramic repair materials.

This study aimed to evaluate the effect of in vitro immersion solutions or an in vivo method on volumetric change of bioceramic root repair materials: Bio-C Repair (BCR, Angelus, Londrina, PR, Brazil) and Biodentine (BIO, Septodont, Saint-Maur-des-Fossés, France) compared to IRM (Dentsply Sirona, York, Pennsylvania, USA) by using microcomputed tomography (µCT) assessment. Tubes of polyvinyl chloride (PVC, 4 mm of length x 1.3 mm of inside diameter, n = 7) were filled with the materials for volumetric analysis in µCT.

Physicochemical properties and antibiofilm activity of mineral trioxide aggregate associated with farnesol.

This study assessed the physicochemical and antibiofilm properties of white mineral trioxide aggregate (MTA) associated with 1 or 2% of farnesol. Setting time was evaluated based on ISO 6876/2012. Radiopacity was evaluated by radiographic analysis.

Filling ability of ready-to-use or powder-liquid calcium silicate-based sealers after ultrasonic agitation.

This study evaluated the effect of ultrasonic agitation on the filling capacity of ready-to-use calcium silicate-based sealer Bio-C Sealer (BCS, Angelus, Paraná, Brazil) or powder-liquid BioRoot RCS (BR, Septodont, Saint-Maur-des-Fossés, France) using curved artificial canals by micro-computed tomography (micro-CT). Additionally, flow (mm) and flow area (mm2) were evaluated for both materials. Acrylic resin main canal (60° curvature and 5 mm radius, with 3 lateral canals in the cervical, middle, and apical thirds) were prepared up to size 40/.

Biocompatibility, bioactivity, porosity, and sealer/dentin interface of bioceramic ready-to-use sealers using a dentin-tube model.

This study evaluated the biocompatibility, bioactivity, porosity, and sealer/dentin interface of Sealer Plus BC (SP), Bio-C Sealer (BIOC), TotalFill BC Sealer (TF), and AH Plus (AHP). Dentin tubes filled with the sealers and empty tubes (control group) were implanted in the subcutaneous tissue of rats for different periods (n = 6 per group/period). Number of inflammatory cells (ICs), capsule thickness, von Kossa reaction, interleukin-6 (IL-6) and osteocalcin (OCN) were evaluated.

Effect of pH on the solubility and volumetric change of ready-to-use Bio-C Repair bioceramic material.

Acidic pH can modify the properties of repair cements. In this study, volumetric change and solubility of the ready-to-use bioceramic repair cement Bio-C Repair (BCR, Angelus, Londrina, PR, Brazil) were evaluated after immersion in phosphate-buffered saline (PBS) (pH 7.0) or butyric acid (pH 4.

Biocompatibility and bioactive potential of NeoPUTTY calcium silicate-based cement: An in vivo study in rats.

Aim: To evaluate the inflammatory reaction and the ability to induce mineralization activity of a new repair material, NeoPUTTY (NPutty; NuSmile, USA), in comparison with Bio-C Repair (BC; Angelus, Brazil) and MTA Repair HP (MTA HP; Angelus, Brazil).

Methodology: Polyethylene tubes were filled with materials or kept empty (control group, CG) and implanted in subcutaneous tissue of rats for 7, 15, 30, and 60 days (n = 6/group). Capsule thickness, number of inflammatory cells (ICs), fibroblasts, collagen content, and von Kossa analysis were performed.

Bioactive potential of Bio-C Temp demonstrated by systemic mineralization markers and immunoexpression of bone proteins in the rat connective tissue.

Intracanal medications are used in endodontic treatment due to their antibacterial activity and ability to induce the periapical repair. Among the intracanal medications, the Calen (CAL; SS. White, Brazil) is a calcium hydroxide-based medication that provides an alkaline pH and releases calcium, exerting an antimicrobial activity.

Flatsonic Ultrasonic Tip Optimizes the Removal of Remaining Filling Material in Flattened Root Canals: A Micro-computed Tomographic Analysis.

Introduction: The aim of this study was to evaluate the effectiveness of the XP-endo Finisher R (XPFR; FKG Dentaire, La Chaux-de-Fonds, Switzerland) or the Flatsonic ultrasonic tip (Helse Ultrasonic, Santa Rosa de Viterbo, SP, Brazil) in removing remaining filling material after the retreatment of flattened root canals using micro-computed tomographic imaging.

Methods: Twenty-four flattened distal root canals of mandibular molars with a buccolingual diameter 4 or more times larger than the mesiodistal diameter were prepared with Reciproc Blue (RB) R40 (VDW GmbH, Munich, Germany) and filled using the Tagger hybrid technique. All canals were retreated with RB R40, and apical enlargement was performed with RB R50 (VDW GmbH).

Effect of Endo-Z bur or Bladesonic ultrasonic tip on the adaptation of filling material. A micro-CT study.

This study aimed to evaluate the effect of apicoectomy performed with a bur or an ultrasonic tip on the adaptation of the filling material to root canal dentin. Twenty human mandibular incisors were selected and prepared with a ProDesign Logic system up to diameter 40/.05.

Diamond-coated ultrasonic tip decreases debris and uninstrumented surface after preparation of curved canals with isthmus.

The aim of this study was to evaluate root canal preparation with nickel titanium rotary instruments and complementary preparation with ultrasonic tip in curved canals of mandibular molars with isthmus. Twenty-eight mesial roots of mandibular molars with curvature between 20° and 40° and presence of isthmus throughout the entire extension of the root canals were prepared using ProDesign Logic CM (PDL) up to size 40.05, or HyFlex EDM (HFEDM) up to size 40.

Effect of radiopacifier and liquid in the physicochemical and biological properties of calcium silicate clinker Angelus: A laboratory investigation.

The aim of this study was to evaluate the effect of radiopacifier calcium tungstate and manipulation with distilled water (DW) or liquid with additives (LA) on calcium silicate clinker Angelus (CL) properties, compared with MTA (Angelus, Brazil) and MTA Repair HP (MTAHP, Angelus, Brazil). The physicochemical properties, cellular viability and bioactivity were evaluated. ANOVA/Tukey and Bonferroni tests were performed (α = 0.

Biocompatibility, bioactive potential, porosity, and interface analysis calcium silicate repair cements in a dentin tube model.

Objectives: This study is to evaluate biocompatibility, bioactive potential, porosity, and dentin/material interface of Bio-C Repair (BIOC-R), MTA Repair HP (MTAHP), and Intermediate Restorative Material (IRM).

Materials And Methods: Dentin tubes were implanted into subcutaneous of rats for 7, 15, 30, and 60 days. Thickness of capsules, number of inflammatory cells (ICs), interleukin-6 (IL-6), osteocalcin (OCN), and von Kossa were evaluated.

Physicochemical properties, cytotoxicity and bioactivity of a ready-to-use bioceramic repair material.

The aim of this study was to evaluate the physicochemical properties, cytotoxicity and bioactivity of a ready-to-use bioceramic material, Bio-C Repair (Angelus), in comparison with White MTA (Angelus) and Biodentine (Septodont). The physicochemical properties of setting time, radiopacity, pH, solubility, dimensional and volumetric changes were evaluated. Biocompatibility and bioactivity were assessed in Saos-2 osteoblast cell cultures by the MTT assay 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide), Neutral Red (NR), Alizarin Red (ARS), and cell migration tests.

Cytotoxicity and bioactive potential of new root repair materials for use with BMP-2 transfected human osteoblast cells.

Modified formulations of calcium silicate repair materials with additives have been developed to enhance handling, consistency, biocompatibility and bioactivity. Considering the relevance of osteoblastic cell response to mineralized tissue repair, human osteoblastic cells (Saos-2 cells overexpressing BMP-2) were exposed to mineral trioxide aggregate (MTA) (with calcium tungstate - CaWO4), MTA HP Repair, Bio-C Repair and Bio-C Pulpo. Cell viability was assessed by 3-(4,5-dimethylthiazol)-2,5-diphenyltetrazolium bromide (MTT) and neutral red (NR), and cell death, by flow cytometry.

Participation of fibroblast growth factor-1 and interleukin-10 in connective tissue repair following subcutaneous implantation of bioceramic materials in rats.

Aim: To evaluate whether the bioceramic materials Bio-C Pulpo (Bio-C, Angelus) and mineral trioxide aggregate (MTA) Repair HP (MTA-HP, Angelus) induce fibroblast proliferation and release of interleukin-10 (IL-10), an anti-inflammatory cytokine, stimulating connective tissue remodelling. The tissue response of Bio-C and MTA-HP was compared with the White MTA (WMTA; Angelus) since studies have demonstrated that WMTA induces tissue repair.

Methodology: Bio-C, MTA-HP and WMTA were inserted into polyethylene tubes and implanted in the subcutaneous tissue of Holtzman rats for 7, 15, 30 and 60 days.

Biocompatibility and bioactive potential of an experimental tricalcium silicate-based cement in comparison with Bio-C repair and MTA Repair HP materials.

Aim: To evaluate the tissue reaction of a tricalcium silicate-based repair material associated with 30% calcium tungstate (TCS + CaWO ) in comparison to Bio-C Repair (Bio-C; Angelus) and to MTA Repair HP (MTA HP; Angelus).

Methodology: Polyethylene tubes filled with one of the materials or left empty (control group, CG) were implanted into the subcutaneous tissues of rats for 7, 15, 30 and 60 days (n = 32/group). The capsule thickness, number of inflammatory cells, collagen content, interleukin-6 (IL-6), osteocalcin (OCN), von Kossa reaction and analysis under polarized light were evaluated.