Material surface conjugated with fibroblast growth factor-2 for pluripotent stem cell culture and differentiation.

Fibroblast growth factor-2 (FGF-2) is a critical molecule for sustaining the pluripotency of human pluripotent stem (PS) cells. However, FGF-2 is extremely unstable and cannot be stored long periods at room temperature. Therefore, the following FGF-2-conjugated cell culture materials were developed to stabilize FGF-2: FGF-2-conjugated polyvinyl alcohol (PVAI-C-FGF) hydrogels and FGF-2-conjugated carboxymethyl cellulose-coated (CMC-C-FGF) dishes. Human induced pluripotent stem (iPS) cells were proliferated on recombinant vitronectin (rVN)-coated PVAI-C-FGF hydrogels and CMC-C-FGF dishes in medium without FGF-2. Human iPS cells could not be cultivated on rVN-coated PVAI-C-FGF hydrogels for more than two passages but could proliferate on rVN-coated CMC-C-FGF dishes. These results indicated that the amount of immobilized FGF-2 and the base cell materials are important, including the amount of immobilized rVN and the conformation of FGF-2 on the surfaces. When human iPS cells were proliferated on rVN-coated CMC-C-FGF surfaces in medium containing no FGF-2 for 10 passages, their pluripotency and potential to differentiate into cells originating from three germ layers were maintained and . Furthermore, the cells could extensively differentiate into cardiomyocytes, which can be used for cardiac infarction treatment in future and retinal pigment epithelium for retinal pigmentosa treatment in future. The FGF-2-immobilized surface could enable human PS cell culture in medium that does not need to contain unstable FGF-2. The amount of FGF-2 immobilization on the rVN-coated CMC-C-5FGF and CMC-C-20FGF dishes was reduced to 93.6 and 52.2 times, respectively, which is less than the conventional amount of FGF-2 used in culture medium for one passage (6 days) of human iPS cell culture. This reduction resulted from the stabilization of unstable FGF-2 by the immobilization of FGF-2, which was achieved by utilizing optimal base materials (CMC), coating materials (rVN) and long-joint segment (PEG4-SPDP) design.