Trace sorbitol-modified nano-silica: Towards nano-nucleation for poly(L-lactic acid).

Nucleating agents, especially those with small particle sizes, are preferred to boost the nucleation density and crystallinity of poly(lactic acid) (PLA) due to its weak crystallization capability. Organophilicly modified nanofillers hardly alter the nucleation and crystallinity of non-isothermally crystallized PLA. Herein, nano-silica adsorbed trace D-sorbitol (m-SiO) as a heterogeneous nucleating agent was melt-mixed with poly(L-lactic acid) (PLLA), and the isothermal and non-isothermal crystallization behavior, as well as crystallization kinetics, were investigated. Transmission electron microscopy (TEM) revealed that m-SiO was uniformly dispersed in the PLA matrix as 100-300 nm clusters. Differential scanning calorimetry (DSC) and polarized optical microscopy (POM) showed that the nucleation rate and density of the non-isothermally crystallized PLLA/m-SiO composites were significantly improved. Despite the fact that m-SiO does not raise the overall non-isothermal crystallization rate, the crystallization temperature and crystallinity of the PLLA/3%m-SiO composite increased from 97.2 °C and 6.8 % for neat PLLA to 108.2 °C and 48.6 % (10 °C/min cooling rate), respectively. The Avrami exponent n of isothermal crystallization remains unchanged, while the crystallization rate increases dramatically. Both isothermal and non-isothermal crystallization have increased activation energies. The heat deflection temperature increased from 59 °C of neat PLLA to 152 °C with a 50 % increase in impact strength.