Article Abstract
Increasing electric vehicle (EV) adoption requires lithium-ion batteries that can be charged quickly and safely. Some EV batteries have caught on fire despite being neither charged nor discharged. While the lithium that plates on graphite during fast charging affects battery safety, so do the internal ionic currents that can occur when the battery is at rest after charging. These currents are difficult to quantify; the external current that can readily be measured is zero. Here we study a graphite electrode at rest after 6C fast charging using operando X-ray microtomography. We quantify spatially resolved current density distributions that originate at plated lithium and end in underlithiated graphite particles. The average current densities decrease from 1.5 to 0.5 mA cm in about 20 min after charging is stopped. Surprisingly, the range of the stripping current density is independent of time, with outliers above 20 mA cm. The persistence of outliers provides a clue as to the origin of catastrophic failure in batteries at rest.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1021/acsnano.3c05470 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Construction of melem/BiVO/g-CN photocatalyst with a conjugated S-scheme charge transfer pathway for boosting photocatalytic activity under LED light irradiation.
Environ Res
September 2025
Center for High Technology Development, Nguyen Tat Thanh University, Ho Chi Minh City Hi-Tech Park, Ho Chi Minh City, Vietnam; Institute of Applied Technology and Sustainable Development, Nguyen Tat Thanh University, Ho Chi Minh City, Vietnam. Electronic address:
The development of novel multijunction heterostructure photocatalysts is critical for the efficient degradation of organic pollutants, attributed to their ability to enhance the separation of photogenerated electron-hole pairs. In our study, a ternary composite, melem/BiVO/g-CN (BVO/CNMH), was synthesized via an acid-soaking method followed by calcination, using g-CN as a sacrificial precursor in the presence of BiVO. This approach yielded a porous, interconnected architecture in BVO/CNMH.
View Article and Find Full Text PDFZnO dual-functional template-assisted construction of hierarchical porous hard carbon anode for high-rate sodium storage.
J Colloid Interface Sci
September 2025
College of New Energy and Materials, State Key Laboratory of Heavy Oil Processing, China University of Petroleum, Beijing, Changping, 102249, China.. Electronic address:
Hard carbon has emerged as the most widely studied and commercialized anode material for sodium-ion batteries (SIBs). However, improving the charge transfer kinetics within the plateau potential range of the hard carbon anode is crucial for the development of fast-charging SIBs. In this study, we prepared a novel composite material, ZAPA-1300, by uniformly mixing starch, asphalt, and zinc oxide (ZnO), followed by a two-step treatment process.
View Article and Find Full Text PDFSynergistic Dual-Carbon Networks Bridged Mn-Doped TiNbO Anode for Fast-Charging Lithium-Ion Batteries.
ACS Appl Mater Interfaces
September 2025
School of Materials and Energy, Guangdong University of Technology, Guangzhou 510006, China.
The development of anode materials for lithium-ion batteries must meet the demands for high safety, high energy density, and fast-charging performance. TiNbO is notable for its high theoretical specific capacity, low structural strain, and exceptional fast-charging capability, attributed to its Wadsley-Roth crystal structure. However, its inherently poor conductivity has hindered its practical application.
View Article and Find Full Text PDFProposed Five-Electron Charge Quadrupole Qubit.
Phys Rev Lett
August 2025
University of Maryland Baltimore County, Department of Physics, Baltimore, Maryland 21250, USA.
A charge qubit couples to environmental electric field fluctuations through its dipole moment, resulting in fast decoherence. We propose the p-orbital (pO) qubit, formed by the single-electron, p-like valence states of a five-electron Si quantum dot, which couples to charge noise through the quadrupole moment. We demonstrate that the pO qubit offers distinct advantages in quality factor, gate speed, readout, and size.
View Article and Find Full Text PDFNanostructured LiNiCoAlO (NCA) for fast-charging, high-capacity battery cathodes.
Nanoscale Horiz
September 2025
Department of Chemistry and Biochemistry, University of California, Los Angeles, California 90095, USA.
Nanostructuring, which shortens lithium-ion diffusion lengths, can help facilitate pseudocapacitive behavior in some battery materials. Here, nanostructured LiNiCoAlO (NCA), with porosity and decreased crystallite size compared to commercial bulk NCA, was synthesized using a colloidal polymer template. Small particles (∼150 nm) were obtained using rapid thermal annealing (RTA), while medium particles (∼300 nm) were obtained with conventional heating.
View Article and Find Full Text PDF