Fusion Separation of Vanadium-Titanium Magnetite and Enrichment Test of Ti Element in Slag.

In view of the problem that the enrichment and migration law of the Ti element in the slag of vanadium-titanium magnetite during the melting process is not clear, the phase transformation is not clear and the enrichment effect is not obvious, the single factor experiment and orthogonal experiment are used to optimize the melting conditions of Ti enrichment. Through XRD, SEM and EDS analysis, the effects of melting temperature, alkalinity and carbon content on the Ti phase in the slag are studied, and the occurrence form and migration law of the Ti element in the slag system under different melting conditions are clarified. The results demonstrate that increasing the basicity and melting temperature is beneficial to the enrichment of Ti, but it is too high it will lead to the formation of pyroxene, diopside and magnesia-alumina spinel, affecting the enrichment of Ti. The increase in carbon content can make Ti occur in slag in the form of titanium oxides such as TiO, TiO, TiO and TiO, but excessive carbon content leads to the excessive reduction of Ti compounds to TiCN and TiC. After optimization, under the melting conditions of alkalinity 1.2, the melting temperature 1500 °C and carbon content 15%, the content of Ti in slag can reach 18.84%, and the recovery rate is 93.54%. By detecting the content of Fe and V in molten iron, the recovery rates are 99.86% and 95.64%, respectively.