Thermostable and nonflammable polyimide/zirconia compound separator for lithium-ion batteries with superior electrochemical and safe properties.

Separators are applied to segregate cathode and anode, and provide ion transport channels in lithium-ion batteries (LIBs). Nevertheless, present commercial polyolefin separators represent high thermal shrinkage and inferior electrolyte wettability, seriously limiting wider development of LIBs. In this work, we prepared zirconia (ZrO) nanolayer encapsulated polyimide (PI) nanofiber compound separator through in-situ polar adsorption and hydrolysis strategy. The obtained PI/ZrO compound separator has superior thermal stability, electrolyte wettability and flame retardance in comparison with polypropylene (PP) separator. The shrinkage ratio of prepared PI/ZrO compound separator is 0 even at 300 °C, while the PP separator significantly shrank at 160 °C. Furthermore, the ionic conductivity of PI/ZrO separator reaches up to 1.32 mS cm, far higher than 0.34 mS cm of PP separator. Besides, the coin batteries of LiNiCoMnO (NCM811)/electrolyte-separator/lithium (Li) assembled with PI/ZrO compound separator exhibit enhanced rate performance, high discharge capacity retention rate of 88.3% after 100 cycles at 1C and excellent battery safety performance even at 140 °C. Thus, combined with its advantages, such as preparation, thermostability, electrolyte wettability, electrochemical property and safety, the PI/ZrO compound separator exhibits promising prospect in the application of commercial LIBs.