Influence of the Cation Ratio on Optical and Electrical Properties of Amorphous Zinc-Tin-Oxide Thin Films Grown by Pulsed Laser Deposition.

Continuous composition spread (CCS) methods allow fast and economic exploration of composition dependent properties of multielement compounds. Here, a CCS method was applied for room temperature pulsed laser deposition (PLD) of amorphous zinc-tin-oxide to gain detailed insight into the influence of the zinc-to-tin cation ratio on optical and electrical properties of this ternary compound. Our CCS approach for a large-area offset PLD process utilizes a segmented target and thus makes target exchange or movable masks in the PLD chamber obsolete. Cation concentrations of 0.08-0.82 Zn/(Zn + Sn) were achieved across single 50 × 50 mm(2) glass substrates. The electrical conductivity increases for increasing tin content, and the absorption edge shifts to lower energies. The free carrier concentration can be tuned from 10(20) to 10(16) cm(-3) by variation of the cation ratio from 0.1 to 0.5 Zn/(Zn + Sn).