Effect of Constant Cyclic Stress Coupling on the Fatigue Behavior of 304LN Stainless Steel.

The stress state of the primary circuit main pipeline is very complex mixed constant stress and periodic cyclic stress during the operation of nuclear power plants, which often affects the failure behavior of the stainless steel (SS) pipe. The fatigue behavior of 304LN SS under mixed constant stress and cyclic stress was investigated, and it was found that the coupling effect of constant stress and cyclic stress has a significant collaborative acceleration on the fatigue behavior. The research results showed that the cracks in the 304LN SS did not propagate even after 78 days under both constant load conditions of 5 KN and 7.

The development of prediction model on irradiation embitterment for low Cu RPV steels.

The development of prediction model on irradiation embitterment (PMIE) of reactor pressure vessel (RPV) is an important method for nuclear reactor long term operation. Based on the physical mechanism of RPV irradiation embrittlement, a preliminary model is determined and the critical threshold of Cu content of 0.072% is obtained according to this preliminary model.