Calcium hydroxide-loaded nanoparticles dispersed in thermosensitive gel as a novel intracanal medicament.

Aim: Design, produce and assess the viability of a novel nanotechnological antibacterial thermo-sensible intracanal medicament This involves encapsulating calcium hydroxide (Ca(OH)) within polylactic-co-glycolic acid (PLGA) nanoparticles (NPs) and dispersing them in a thermosensitive gel (Ca(OH)-NPs-gel). In addition, perform in vitro and ex vivo assessments to evaluate tissue irritation and penetration capacity into dentinal tubules in comparison to free Ca(OH).

Methodology: Reproducibility of Ca(OH)₂-NPs was confirmed by obtaining the average size of the NPs, their polydispersity index, zeta potential and entrapment efficiency.

Novel strategies enhancing endodontic disinfection: Antibacterial biodegradable calcium hydroxide nanoparticles in an ex vivo model.

Due to the high failure rates associated to endodontic disinfection, this study aimed to investigate the antibacterial properties of poly(lactic-co-glycolic acid) (PLGA) nanoparticles (NPs) loaded with Ca(OH) for endodontic disinfection procedures. Ca(OH) NPs production and physicochemical characterization were carried out as well as multiple antibacterial tests using three bacterial strains and an ex vivo model of endodontic infection with extracted human teeth. Agar diffusion test and broth dilution determined the inhibition growth zones (n = 5) and the minimal inhibitory concentration (MIC, n = 5), respectively.

Restoration's thickness and bonding tooth substrate are determining factors in minimally invasive adhesive dentistry.

Purpose To explore fracture strength and failure behaviour of minimally invasive CAD-CAM composite resin overlay restorations.Methods Eighty bi- and tri-layer cylindrical overlay model including the restoration bonded over bovine tooth dentin (Groups D) and enamel-dentin (Groups E) were assembled (diameter 9 mm). Restorations were milled from CAD-CAM composite resin blocks (Brilliant Crios, Coltène/Whaledent AG) in different thicknesses (0.